CuNi10Fe1Mn1-B ( CB380H )
| CuNi10Fe1Mn1-B | |
| CB380H | |
| Copper-nickel alloy | |
| EN 1982: 2008 Copper and copper alloys. Ingots and castings | |
Chemical composition % of grade CuNi10Fe1Mn1-B ( CB380H )
| A suffix -B is added to the designation to identify material in the form of ingots |
| C | |||||||||
| 1.2 - 1.8 | max 0.1 | max 0.1 | 1.2 - 1.5 | 9.2 - 11 | max 1 | max 0.01 | min 84.5 | max 0.03 | max 0.5 |
Mechanical properties of grade CuNi10Fe1Mn1-B ( CB380H )
| - Tensile strength (MPa) (GS) | 280 |
| - Tensile strength (MPa) (GZ) or (GC) | 280 |
| Rp0.2 0.2% proof strength (MPa) (GS) | 120 |
| Rp0.2 0.2% proof strength (MPa) (GZ) or (GC) | 100 |
| A - Min. elongation at fracture (%) (GS) | 20 |
| A - Min. elongation at fracture (%) (GZ) or (GC) | 25 |
| 70 |
| R | |
| H |
| R | |
| Rm | |
| A | |
| J |
|
CuNi10Fe1Mn1-B ( CB380H ) Copper-nickel alloy |