Titanium is an allotropic isomer with a melting point of 1668℃. It shows a dense row hexagonal lattice structure called -titanium when it is lower than 882℃, and it shows a body-centered cubic lattice structure called -titanium when it is above 882℃. The use of titanium's different characteristics of the above two structures, add the appropriate alloying elements, so that the phase transition temperature and phase content gradually change and get different organizations of titanium alloys. At room temperature, titanium alloys have three kinds of matrix organization, and titanium alloys are divided into the following three categories: -alloys, ( + ) alloys and -alloys. In China, they are expressed as TA, TC and TB respektive .
titanlegering
It is a single-phase alloy composed of -phase solid solution, which is -phase both at general temperature and at higher temperature of practical application, with stable organization, higher wear resistance than pure titanium, and strong oxidation resistance. Under the temperature of 500℃-600℃, it still maintains its strength and creep resistance, but it cannot be strengthened by heat treatment, and its room temperature strength is not hög .
titanlegering
Det är en enfaslegering sammansatt av fasfasig lösning, som har hög styrka utan värmebehandling, och legeringen stärks ytterligare efter kylning och åldrande, och rumstemperaturstyrkan kan vara upp till 1372-1666 MPA; Det har emellertid dålig termisk stabilitet, och den är inte lämplig att användas vid höga temperaturer .
+ Titanlegering
Det är en dubbelfaslegering med god omfattande prestanda, god organisatorisk stabilitet, god seghet, plasticitet och högtemperaturdeformationsegenskaper, kan vara bättre varmtrycksbehandling, kylning, åldrande för att göra legeringen stärkt . Styrkan efter värmebehandling är cirka 50% till 100% högre än det analiska tillståndet; Hög hög temperaturstyrka, kan arbeta länge vid en temperatur på 400 grader till 500 grader, och dess termiska stabilitet är den andra till den för titanlegering .
De vanligaste av de tre titanlegeringarna är -Titaniiumlegering och + - titanlegering; -titanium alloy has the best machinability, + -titanium alloy is the second best and -titanium alloy is the worst. -titanium alloy is codenamed TA, -titanium alloy is codenamed TB and + -titanium alloy is codenamed TC.
Titanium alloys can be divided into heat-resistant alloys, high-strength alloys, corrosion-resistant alloys (titanium-molybdenum, titanium-palladium alloys, etc.), low-temperature alloys, and special functional alloys (titanium-iron hydrogen storage materials and titanium-nickel memory alloys).
Värmebehandling: Titanlegeringar kan erhålla olika faskompositioner och organisationer genom att justera värmebehandlingsprocessen . Det tros generellt att den fina isometriska organisationen har bättre plasticitet, termisk stabilitet och trötthetsstyrka; Nålliknande organisation har högre uthållighetsstyrka, kryphållfasthet och fraktursughet; Isometrisk och nålliknande blandad organisation har bättre totalprestanda .
Ny titanlegering
Neotitanium alloys consist of a mixture of two types of titanium crystals, called -titanium phase and -titanium phase, each corresponding to a specific atomic arrangement. Oxygen and iron are the two most powerful stabilizers and strengtheners of the -titanium phase and the -titanium phase, and they are abundant and inexpensive.